PA6-CF vs PA6-GF - Impact Toughness vs Brittleness (fosscad.io)

submitted 2 months ago by gsgmfg@fosscad.io to c/general

10 comments fedilink hide all child comments

Reading through this thread: https://forum.bambulab.com/t/gf-vs-cf-pros-and-cons/192469

What's the consensus on PA6-GF vs CF?

I'm mostly interested in optimizing Super Safety Components like the lever for impact resistance, but also anti-warping.

Currently using PA6-CF. Having solidish results.

PLA+ lever warped (but didn't break) after 450 rounds of .300blk. Very gassy with a can.

Still need to do more solid testing with PA6-CF.

Both material levers break if I smack em with a mallet on an anvil - but that seems like a shitty metric either way.

you are viewing a single comment's thread
view the rest of the comments

[–] gsgmfg@fosscad.io 1 points 2 months ago

Yeah that chart is a little fucky. It came from a thread discussing PETG-GF vs PA6-CF - and I was curious about the ductility improvements of the GF.

Even at the cost of overall strength. But it seems the brittleness is not that different.